For high-strength connection of cylindrical parts subject to high loads
Reliable hardening at low temperatures around 0°C

A reliable “helper” in winter, too

High degree of gap bridging

Completely fills extensive surface roughnesses

Gap filling capacity of 0.15 mm

Even extremely large deviations are cost effective to correct.

Prevents frictional corrosion

The bearings will not seize up.

Resistant to a large number of bases, gases, solvents, oils and fuels

Silicone-free, solvent-free and oil-free

DOS system:

Practical one-handed operation thanks to the clever turn lock
One hand always remains free.

Continuously adjustable dispensing system
Dispensing can be adjusted to suit the application, and to keep consumption and costs to a minimum.

No residue material in dispensing neck
Costs optimised thanks to emptying with virtually no remaining product

The following plastics can be affected in the event of prolonged exposure: ABS, celluloid, polystyrene, polycarbonate (Macrolon), PMMA (Plexiglas), polysulfone, SAN (lurane, Tyril), Vinidur, vulcanised fibre, and painted surfaces. We always recommend that you conduct your own tests.

NSF-registered, Class S5, bearing retaining compound
NSF-tested in accordance with NSF/ANSI 61 for use in service water and drinking water up to +82°C
The usage instructions are recommendations based on the tests we have conducted and on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. If our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee the consistent quality of our products. We reserve the right to make technical changes and further develop products.

Please observe the technical data sheet!

Weight of content

25 g

Chemical basis

Methacrylic acid ether




1.07 g/cm³ / in accordance with DIN EN ISO 2811-1

Suitable for max. thread


Max. gap-filling ability

0.15 mm

Min./max. viscosity /conditions

100-200 mPas / at 25°C, Brookfield RVT, spindle 2/20 rpm

Fully hardening/curing conditions

Exclusion of oxygen and contact with metal (copper or iron ions)

Min./max. initial strength

5-10 min

Min./max. functional strength

30-40 min

Min./max. final strength

3 h-6 h

Min./max. processing temperature

5 to 35 °C

Min./max. temperature conditions

-55 to 150 °C

Min. flashing point

90 °C

Min. prevail torque

35 Nm

Conditions for prevail torque

DIN EN 15865

Shelf life from production/conditions

18 Month / at room temperature








There are no reviews yet.

Be the first to review “WURTH 0893603025 HIGH-STRENGTH BEARING LOCKING 25g.”

Your email address will not be published. Required fields are marked *

Exclusive Offer Just for You!

A Special Gift Awaits on Orders Over €150
For every order exceeding €150, we’re excited to gift you a complimentary Loctite 5970 (50ml). It’s our way of saying ‘thank you’ for choosing us.